ASTM A213 qotishma quvurlari odatda energiya ishlab chiqarish, neft-kimyo, farmatsevtika va kimyoviy qayta ishlash sanoatida qo'llaniladi. Ular yuqori harorat va bosimlarda mukammal oksidlanish va korroziyaga chidamliligiga ega, bu ularni og'ir muhitda foydalanish uchun ideal qiladi.
ASTM SA213 po'lat quvur tavsifi
ASTM A213 qotishma po'lat quvurlari (SA213, Chorme-Moly) yuqori haroratli ilovalar uchun choksiz ferritli qotishma po'lat quvurdir. Ushbu SA213 materiallari egilish, flanging (vanstoning) va shunga o'xshash shakllantirish operatsiyalari, shuningdek, energetika sanoati va neft-kimyo zavodlarida termoyadroviy payvandlash kabi yuqori haroratli ilovalar uchun javob beradi. SA213 qotishma po'lat quvur, shuningdek, molibden (Mo) va xrom (Cr) ning kimyoviy tarkibi tufayli ASTM A213 xrom-molibden quvuri sifatida ham tanilgan. Molibden ASME SA213 kvadrat quvurlarining mustahkamligini, shuningdek, uning elastik chegarasi, aşınma qarshiligi, zarba sifati va qotib qolish qobiliyatini saqlaydi. Molibden ASTM A213 trubkasining yuqori haroratli o'tish kuchini yaxshilash uchun yagona samarali qo'shimcha hisoblanadi.
SA213 qotishma po'lat quvurlari spetsifikatsiyasi
|
Material: |
A36, A53, A106, A192, ST52, Q355, A210, T12, T11, P5, P9, P91, T22, A333, 4140, 5135 va boshqalar. |
|
|
Darajasi (EN): |
1.7220,1.7336,1.2601,1.7380,1.7335,1.0033,1.0116 va boshqalar. |
|
|
Hajmi |
Tashqi diametri |
Uzluksiz:17-914mm 3/8"-36" |
|
Devor qalinligi |
% 7b{0}}mm SCH10 SCH20 SCH30 STD SCH40 SCH60 XS SCH80 |
|
|
Uzunlik |
1-12m mijoz talabi sifatida |
|
|
Tugaydi |
To'g'ri uchi / qiyshiq, ikkala uchida plastik qopqoqlar bilan himoyalangan, kesilgan, yivli, tishli va muftali va boshqalar. |
|
|
Yuzaki ishlov berish |
Yalang'och, bo'yash qora, laklangan, galvanizli, korroziyaga qarshi 3PE PP/EP/FBE qoplamasi |
|
|
Texnik usullar |
Issiq haddelenmiş / Sovuq chizilgan / Issiq kengaytirilgan |
|
|
Sinov usullari |
Bosim sinovi, nuqsonlarni aniqlash, girdobli oqim sinovi, gidrostatik sinov yoki ultratovush tekshiruvi, shuningdek kimyoviy va |
|
|
Uchinchi tomon tekshiruvi |
SGS BV MTC |
|
|
Savdo shartlari |
FOB CIF CFR |
|
|
To'lov shartlari |
FOB 30% T / T, jo'natishdan oldin 70% |
|
|
CIF 30% oldindan to'lov va qoldiq B/L da to'lanishi kerak (nusxa) |
||
|
yoki qaytarib bo'lmaydigan 100% L/C ko'rishda |
||
SA213 po'lat quvur
Mahsulot parametrlari
Qotishma po'latdan ASTM A213 quvurining kimyoviy tarkibi:
|
Baho |
C |
Mn |
P |
S |
Si |
Cr |
Moʻy |
V |
N |
Ni |
Al |
Nb |
W |
|
T2 |
0.10-0.20 |
0.30-0.61 |
0.025 maks |
0.025 maks |
0.10-0.30 |
0.50-0.81 |
0.44-0.65 |
|
|
|
|
|
|
|
T5 |
0.15 maks |
0.30-0.60 |
0.025 maks |
0.025 maks |
0.50 maks |
4.00-6.00 |
0.45-0.65 |
|
|
|
|
|
|
|
T9 |
0.15 maks |
0.30-0.60 |
0.025 maks |
0.025 maks |
0.25-1.00 |
8.0-10.0 |
0.90-1.10 |
|
|
|
|
|
|
|
T11 |
0.15 maks |
0.30-0.60 |
0.025 maks |
0.025 maks |
0.50-1.00 |
1.00-1.50 |
0.44-0.65 |
|
|
|
|
|
|
|
T12 |
0.15 maks |
0.30-0.60 |
0.025 maks |
0.025 maks |
0.50-1.00 |
1.00-1.50 |
0.44-0.65 |
|
|
|
|
|
|
|
T22 |
0.05-0.15 |
0.30-0.60 |
0.025 maks |
0.025 maks |
0.50 maks |
1.90-2.60 |
0.87-1.13 |
|
|
|
|
|
|
|
T91 |
0.08-0.12 |
0.30-0.60 |
0.020 maks |
0.010 maks |
0.20-0.50 |
8.00-9.50 |
0.85-1.05 |
0.18-0.25 |
0.03-0.07 |
0.40 maks |
0.04 maks |
0.06-0.10 |
|
|
T92 |
0.07-0.13 |
0.30-0.60 |
0.020 maks |
0.010 maks |
0.50 maks |
8.50-9.50 |
0.30-0.60 |
.015-0.25 |
0.03-0.07 |
0.40 maks |
0.04 maks |
0.04-0.09 |
1.50-2.00 |
ASTM A213 qotishma po'lat quvur mexanik xususiyatlari jadvali:
|
Baho |
Kuchlanish kuchi, Mpa |
Hosildorlik kuchi, Mpa |
Cho'zilish, % |
Qattiqlik, HB |
|
T2 |
415 min |
205 min |
30 min |
163 maksimal |
|
T5 |
415 min |
205 min |
30 min |
163 maksimal |
|
T9 |
415 min |
205 min |
30 min |
179 maksimal |
|
T11 |
415 min |
205 min |
30 min |
179 maksimal |
|
T12 |
415 min |
205 min |
30 min |
179 maksimal |
|
T22 |
415 min |
205 min |
30 min |
163 maksimal |
|
T91 |
585 min |
415 min |
20 min |
250 maks |
|
T92 |
585 min |
415 min |
20 min |
250 maks |
ASTM A213 qotishma trubkasi tashqi diametri bardoshliligi:
|
Usul |
Tashqi diametri, mm |
Tolerantlik, mm |
|
Issiq haddelenmiş |
OD% 7b{0}}.6 |
+0.4 / -0.8 |
|
101.6<> |
+0.4 / -1.2 |
|
|
190.5<> |
+0.4 / -1.6 |
|
|
Sovuq chizilgan |
OD<25.4 |
±0.10 |
|
25.%4=OD=38.1 |
±0.15 |
|
|
38.1<> |
±0.20 |
|
|
50.8=OD<63.5 |
±0.25 |
|
|
63.5=OD<76.2 |
±0.30 |
|
|
76.2=OD=101.6 |
±0.38 |
|
|
101.6<> |
0.38 / -0.64 |
|
|
190.5<> |
0.38 / -1.14 |
|
ASTM A213 po'lat quvur devor qalinligi bardoshliligi:
|
Usul |
Tashqi diametri, mm |
Tolerantlik, % |
|
Issiq haddelenmiş |
OD% 7b{0}}.6,WT=2.4 |
+40 / -0 |
|
OD% 7b{0}}.6,2.4<> |
+35 / -0 |
|
|
OD% 7b{0}}.6,3.8<> |
+33 / -0 |
|
|
OD=101.6,WT>4.6 |
+28 / -0 |
|
|
OD>101.6,2.4<> |
+35 / -0 |
|
|
OD>101.6,3.8<> |
+33 / -0 |
|
|
OD>101.6,WT>4.6 |
+28 / -0 |
|
|
Sovuq chizilgan |
OD% 7b{0}}.1 |
+20 / -0 |
|
OD>38.1 |
+22 / -0 |
Kompaniya fotosurati
GNEE guruhi zanglamaydigan po'lat quvur, qotishma quvur, uglerod po'lat quvur va boshqalar kabi har xil turdagi po'lat quvur mahsulotlarini taqdim etishi mumkin. Bizning issiq navlarimiz A213, A312, A333, A335, API 5L, A53, A36 va boshqalar.
Issiq teglar: qotishma po'lat quvurlari, Xitoy qotishma po'lat quvurlari ishlab chiqaruvchilari, etkazib beruvchilari, zavodi